Intuthu Ephansi Zero Halogen Optical Cable Material, Cable Cable Material (LSZH Optical Cable Material, Network Cable Material)
IZICI ZOMKHIQIZO
UMHLABA WOKUSETSHENZISWA
Izinto zokuhlola namazinga
|
| Into yokuhlola | Iyunithi | Rizidingo | ||
| WDZ-Y-J70 | WDZ-Y-H70 | WDZ-Y-H90 | |||
| 1 | Amandla aqinile | I-MPa | ≥10. 0 | ≥10. 0 | ≥10. 0 |
| 2 | Ukwandisa ngesikhathi sekhefu | % | ≥160 | ≥160 | ≥160 |
| 3 | Igumbi lokuguga lomoya |
|
|
|
|
| Izinga lokushisa lokuguga | ℃ | 100±2 | 100±2 | 110±2 | |
| Isikhathi sokuguga | h | 168 | 168 | 240 | |
| Izinga eliphezulu lokushintsha kwamandla e-tensile | % | ±25 | ±25 | ±25 | |
| Izinga eliphezulu lokushintsha ubude ngesikhathi sekhefu | % | ±25 | ±25 | ±25 | |
| 4 | Ukuguqulwa kwe-thermal |
|
|
|
|
| Hlola izinga lokushisa | ℃ | 90±2 | 90±2 | 90±2 | |
| Umphumela wokuhlola | % | ≤50 | ≤50 | ≤50 | |
| 5 | 20 ℃ ivolumu ukumelana | Oh · m | ≥1. 0×1012 | ≥1. 0×1010 | ≥1. 0×1010 |
| 6 | Ukumelana nevolumu kumazinga okushisa okusebenza |
|
|
|
|
| Hlola izinga lokushisa | ℃ | 70±1 | - | - | |
| Ukumelana nevolumu | Oh · m | ≥2. 0×108 | - | - | |
| 7 | Amandla e-Dielectric | MV/m | ≥20 | ≥18 | ≥18 |
| 8 | Ukuhlolwa kokushaqeka kokushisa |
|
|
|
|
| Hlola izinga lokushisa | ℃ | 130±3 | 130±3 | 130±3 | |
| Isikhathi sokuhlola | % | 1 | 1 | 1 | |
| Umphumela wokuhlola | - | Akukho ukuqhekeka | Akukho ukuqhekeka | Akukho ukuqhekeka | |
| 9 | Izinga lokushisa lokuthinta i-embrittlement |
|
|
|
|
| Hlola izinga lokushisa | ℃ | -25 | -25 | -25 | |
| Umphumela wokuhlola | Inombolo | ≤15/30 | ≤15/30 | ≤15/30 | |
| 10 | Ukuhlolwa kokumelana ne-ozone |
|
|
|
|
| Hlola izinga lokushisa | ℃ | - | 25±2 | 25±2 | |
| Isikhathi sokuhlola | h | - | amashumi amabili nane | amashumi amabili nane | |
| Ukuhlushwa kwe-ozone | ppm | - | 250-300 | 250-300 | |
| Umphumela wokuhlola | - | - | Akukho ukuqhekeka | Akukho ukuqhekeka | |
| 11 | Ukuhlolwa kokucwiliswa kwamanzi ashisayo |
|
|
|
|
| Hlola izinga lokushisa | ℃ | - | 70±2 | 70±2 | |
| Isikhathi sokuhlola | h | - | 168 | 168 | |
| Izinga eliphezulu lokushintsha kwamandla e-tensile | % | - | ±30 | ±30 | |
| Izinga eliphezulu lokushintsha ubude ngesikhathi sekhefu | % | - | ±35 | ±35 | |
| 12 | Inkomba ye-oxygen | % | ≥28 | ≥30 | ≥30 |
| 13 | Ukuminyana kwentuthu |
|
|
|
|
| engenamalangabi | - | ≤350 | ≤350 | ≤350 | |
| elivutha amalangabi | - | ≤100 | ≤100 | ≤100 | |
| 14 | Ukushiswa kukhipha i-asidi yegesi |
|
|
|
|
| Okuqukethwe kwe-HCI ne-HBr | % | ≤0.5 | ≤0.5 | ≤0.5 | |
| Okuqukethwe kwe-HF | % | ≤0.1 | ≤0.1 | ≤0.1 | |
| Inani le-pH | - | ≥4.3 | ≥4.3 | ≥4.3 | |
| I-conductivity kagesi | μS/mm | ≤10 | ≤10 | ≤10 | |
| 15 | Izingozi zobungozi bentuthu | Ngokwezidingo zokusetshenziswa komkhiqizo, okuxoxiswene ngazo yizinkampani ezihlinzekayo nezifunayo. | |||