Ijeli yokugcwalisa i-Optical Fiber ebandayo
Isingeniso Somkhiqizo
Isingeniso somkhiqizo: Ijeli yokugcwalisa i-fiber optical isebenzisa uwoyela wenqubo ye-viscosity GTL ephezulu, izinto zokwenziwa zamangqamuzana aphezulu kanye ne-organic thickener njengezisetshenziswa eziyisisekelo. Zihlanganiswe zibe ijeli yokugcwalisa i-non-silicon optical fiber ngenqubo yokukhiqiza ethuthukisiwe izici zayo eziwukuminyana okuphansi, ukusebenza kahle kwezinga lokushisa, inkomba ephezulu ye-thixotropic, ukusetshenziswa okubanzi, inani le-asidi elincane kanye nenani lokuvela kwe-hydrogen. Uhlobo lwe-AC-E008 nalo lusebenza kancane kancane izinga lokushisa phakathi kuka--45°C kuya ku-80°C. Ngokwezidingo ezahlukahlukene zamaklayenti, inkomba yezobuchwepheshe ye-viscosity, ukungena, i-thixotropic nokunye kungalungiswa ukuze kwenelise izidingo zendlela yokugcwalisa.
Imingcele yezobuchwepheshe
Isicelo esibandayo se-fiber optical fibre filling gel ukucaciswa kobuchwepheshe
1, izidingo zobuchwepheshe ezijwayelekile
Ijeli yokugcwalisa iyadingeka ukuze ibe ne-homogeneous, ukumuncwa kwe-hydrogen, futhi ayifaki noma yiluphi uthuli, izinhlayiya zensimbi, nokunye ukungcola. Akufanele kube amabhamuza omoya abonakalayo, futhi isikhunta akufanele sibe nomsoco. Ukugcwalisa ijeli akufanele kube yingozi, kungabikho ukugqugquzela esikhumbeni.
2, imingcele yobuchwepheshe eyinhloko
I-serial Inombolo | Izinto | Iyunithi | Inkomba |
1 | ukubukeka | I-homogeneous, akukho ukungcola | |
2 | Indawo yokulahla | ℃ | ≥200 |
3 | ukuminyana(20℃) | g/cm2 | ≤0.88 |
4 | Ukungena kwekhoni 25℃-40 ℃ | 1/10mm 1/10mm | ≥400 ≥230 |
5 | Ukuzinza kombala(130 ℃,120h) | ≤2.5 | |
6 | Isikhathi sokungeniswa kwe-oxidation(190 ℃) | imiz | ≥30 |
7 | Iphoyinti elikhanyayo | ℃ | ≥220 |
8 | Ukuguquguquka kwe-hydrogen(80℃,24h) | μl/g | ≤0.03 |
9 | Ukujuluka kwamafutha(80℃,24h) | % | ≤0.5 |
10 | Amandla wokuhwamuka(80℃,24h) | % | ≤0.5 |
11 | Ukumelana namanzi(20℃,7d) | Ukungahlakazi | |
12 | Inani le-Acid | mgK0H/g | ≤0.3 |
13 | Okuqukethwe kwamanzi | % | ≤0.01 |
14 | i-viscosity(25℃,D=6S-1) | mpa.s | 22000±6600 |
15 | ukuhambisana:A,nge-fiber optical, opticalizinto zokumboza i-fiber(85℃,30×24h)B,nge-pine casingimpahla(85℃,30×24h)ukuhlukahluka kokuqina kwamandla e-elongation at break mass variation C,Ibhande lensimbi elihlanganisiwe (68℃,7x24h)Itheyiphu eyinhlanganisela yensimbi-yepulasitiki,Ipulasitiki ye-aluminiumi-tape ehlanganisiwe | % % % | Awukho umbala ofiphalayo, Akukho ukufuduka, akukho delamination, akukho ukuqhekeka Amandla okukhululwa aphezulu 1.0N~8.9NInani elimaphakathi 1.0N~5.0Nakukho delamination akukho ukuqhekeka ≤25 ≤30 ≤3 akukho delamination akukho ukuqhekeka |
16 | okudlayo(80℃,14×24h)ngethusi, i-aluminium, insimbi | Awekho amaphuzu okugqwala |
3, Izidingo zokusebenza kwemvelo
Uhlobo | udaba | Okuqukethwe okwenqabelayo(mg/kg) |
Insimbi enzima | umbhobho | ≤1000 |
i-cadmium | ≤100 | |
i-mercury | ≤1000 | |
I-chromium ene-hexavalent | ≤1000 | |
I-Organic Bromide | Ama-biphenyl ane-polybrominated(UN) | ≤1000 |
I-polybrominated diphenyl ethers(I-PBDE) | ≤1000 |