LSZH alawọ ila okun ohun elo

Ohun kan ayewo

Ẹyọ

Rawọn ibeere

WDZ-Y-J70

WDZ-Y-H70

WDZ-Y-H90

1

Agbara fifẹ

MPa

≥10. 0

≥10. 0

≥10. 0

2

Elongation ni isinmi

%

≥160

≥160

≥160

3

Iyẹwu ti ogbo afẹfẹ

otutu ti ogbo

℃

100±2

100±2

110±2

Akoko ti ogbo

h

168

168

240

Iwọn iyipada ti o pọju agbara fifẹ

%

± 25

± 25

± 25

Iwọn ti o pọju ti iyipada elongation ni isinmi

%

± 25

± 25

± 25

4

Ibajẹ gbona

Ṣe idanwo iwọn otutu

℃

90±2

90±2

90±2

Esi esiperimenta

%

≤50

≤50

≤50

5

20 ℃ iwọn didun resistivity

Oh · m

≥1. 0×10¹²

≥1. 0×10¹⁰

≥1. 0×10¹⁰

6

Atako iwọn didun ni iwọn otutu iṣẹ

Ṣe idanwo iwọn otutu

℃

70±1

-

-

resistivity iwọn didun

Oh · m

≥2. 0×108

-

-

7

Dielectric agbara

MV/m

≥20

≥18

≥18

8

Ooru mọnamọna igbeyewo

Ṣe idanwo iwọn otutu

℃

130±3

130±3

130±3

Akoko idanwo

%

1

1

1

Esi esiperimenta

-

Ko si sisan

Ko si sisan

Ko si sisan

9

Ipa otutu embrittlement

Ṣe idanwo iwọn otutu

℃

-25

-25

-25

Esi esiperimenta

Nọmba

≤15/30

≤15/30

≤15/30

10

Osonu resistance igbeyewo

Ṣe idanwo iwọn otutu

℃

-

25±2

25±2

Akoko adanwo

h

-

mẹrin-le-logun

mẹrin-le-logun

Ozone ifọkansi

ppm

-

250-300

250-300

Esi esiperimenta

-

-

Ko si sisan

Ko si sisan

11

Igbeyewo immersion omi gbona

Ṣe idanwo iwọn otutu

℃

-

70±2

70±2

Akoko adanwo

h

-

168

168

Iwọn iyipada ti o pọju agbara fifẹ

%

-

± 30

± 30

Iwọn ti o pọju ti iyipada elongation ni isinmi

%

-

± 35

± 35

12

Atẹgun itọka

%

≥28

≥30

≥30

13

Ẹfin iwuwo

alailagbara

-

≤350

≤350

≤350

gbigbona

-

≤100

≤100

≤100

14

Ijona n tu acidity gaasi silẹ

HCI ati HBr akoonu

%

≤0.5

≤0.5

≤0.5

HF akoonu

%

≤0.1

≤0.1

≤0.1

iye pH

-

≥4.3

≥4.3

≥4.3

Ina elekitiriki

μS/mm

≤10

≤10

≤10

15

Awọn eewu eewu eefin eefin ohun elo

Gẹgẹbi awọn ibeere ohun elo ti ọja, idunadura nipasẹ ipese ati awọn ẹgbẹ eletan.