Ọja Ifihan
Ifihan ọja: Gel kikun okun USB gba epo ilana GTL ati ohun elo sintetiki molikula giga bi awọn ohun elo ipilẹ akọkọ. Wọn ti wa ni idapo lati jẹ rirọ, iki-kekere, itọka thixotropic giga, gel ti o ni kikun ti ko ni awọ nipasẹ ilana iṣelọpọ ilọsiwaju ti awọn ẹya ara ẹrọ ti o ni ifunra omi, imọ-ẹrọ processing ti o dara julọ ati awọn ohun-ini iwọn otutu giga- ati kekere. O le jẹ rirọ labẹ -40 ℃ ati pe ko si-drip lori iwọn otutu giga ti 80 ℃. Ilana kikun jẹ rọrun eyiti o le kun ni iwọn otutu gbogbogbo, paapaa dara fun apofẹlẹfẹlẹ USB pato ati mojuto USB. Gẹgẹbi ọpọlọpọ awọn ibeere ti awọn alabara, atọka imọ-ẹrọ ti iki, ilaluja, thixotropic ati bẹbẹ lọ ti o le ṣatunṣe lati ni itẹlọrun awọn ibeere ti ilana kikun.
Imọ paramita
Ohun elo Tutu Okun Opitika Filling Gel Technical Specification
1, Gbogbogbo Imọ ibeere
A nilo gel kikun lati jẹ isokan, gbigba hydrogen, ati pe ko pẹlu eruku eyikeyi, awọn patikulu irin, ati awọn aimọ miiran. Ko yẹ ki o jẹ oju awọn nyoju afẹfẹ ti o han, ati pe mimu ko yẹ ki o jẹ ounjẹ. Geli kikun yẹ ki o jẹ ti kii ṣe majele, ko si itara si awọ ara.
2, akọkọ imọ sile
ahoro Nọmba | Awọn nkan | ẹyọkan | Atọka |
1 | irisi | Isọpọ, ko si awọn aimọ | |
2 | Ojuami sisọ | ℃ | ≥150 |
3 | iwuwo (20℃) | g:cm2 | ≤0.96 |
4 | Konu ilaluja 25℃ 40℃ | 1:10mm 1:10mm | ≥300 ≥100 |
5 | Akoko ifasilẹ Oxidation (190 ℃) | min | ≥30 |
6 | Aaye ìmọlẹ | ℃ | >200 |
7 | Itankalẹ hydrogen (80℃, 24h) | μl:g | ≤0.03 |
8 | Opo epo (80℃, 24h) | % | ≤2.0 |
9 | Agbara evaporation (80℃, 24h) | % | ≤1.0 |
10 | Akoko gbigba 25 ℃ (apẹẹrẹ 15g + 10g omi) | min | ≤2.0 |
11 | Dilatation 25 ℃ 5r 100g apẹẹrẹ + 50g omi 24h | % % | ≥15≥70 |
12 | Iye acid | mgK0H:g | ≤1.0 |
13 | Omi akoonu | % | ≤0.1 |
14 | iki (25℃, D=20S-1) | mpa.s | 10500-30000 |
15 | ibamu: A, pẹlu Pine casing ohun elo (85 ℃, 30 × 24h) B, pẹlu Pine casing ohun elo (85℃, 45×24h) iyatọ ninu fifẹ elongation ni Bireki ibi-iyatọ B, pẹlu Pine casing ohun elo 80 28 × 24h) iyatọ ni elongation agbara fifẹ ni iyatọ ibi-fọọmu C, Ẹgbẹ irin idapọpọ (68 ℃, 7 × 24h) Teepu apapo irin-ṣiṣu, teepu aluminiomu ṣiṣu aluminiomu | % % % % % | no delamination no cracking ≤25 ≤30 ≤3 ko si sisan ≤25 ≤25 ≤15 |
15 | ipata (80℃, 14×24h) pẹlu Ejò, aluminiomu, irin | Ko si awọn aaye ipata |
3, Awọn ibeere iṣẹ ṣiṣe ayika
Iru | ọrọ | akoonu idinamọ (mg/kg) |
Irin eru | plumbic | ≤1000 |
cadmium | ≤100 | |
Makiuri | ≤1000 | |
chromium hexavalent | ≤1000 | |
Organic Bromide | Awọn biphenyls polybrominated (PBB) | ≤1000 |
Awọn ethers diphenyl polybrominated (PBDE) | ≤1000 |