I-Polyvinyl Chloride Insulated Cable Material (i-PVC Insulated Cable Material)
IIMPAWU ZEMVELISO
UMDA WOKUSEBENZISA
Izinto zovavanyo kunye nemigangatho
Iune |
| J-70 | JR-70 | JGD-70 | J-90 |
Amandla okuqina/MPa | ≥ | 15.0 | 15.0 | 16.0 | 16.0 |
Ukuxinezeleka ngexesha lokuphumla/% | ≥ | 150 | 180 | 150 | 150 |
Thermal deformation | ≥ | 40 | 50 | 30 | 30 |
Ipropati Brittle tbubushushu/℃ |
| -15 | -20 | -15 | -15 |
Impembelelo iimpawu ze-embrittlement |
| Dlula | Dlula | Dlula | Dlula |
Ixesha lokuzinza kweThermal kwi-200℃/imiz | ≥ | 60 | 60 | 100 | 180 |
Ukuxhathisa umthamo kwi-20℃/Ω·m | ≥ | 1.0×10 12 | 1.0×10 11 | 3.0×1012 | 1.0×10 12 |
Amandla eDielectric/(MV/m) | ≥ | 20 | 20 | 25 | 20 |
Ilahleko yeDielectric factor (50Hz) | ≤ | - | - | 0.1 | - |
Uvavanyo lobushushu/℃ |
| 70±1 | 70±1 | 70±1 | 95±1 |
Ukuxhathisa umthamo/Ω·m | ≥ | 1.0×10 9 | 1.0×108 | 5.0×109 | 5.0×108 |
Iimpawu zoomatshini kunye nezomzimba ze-polyvinyl chloride cable material emva kokuguga
Iune |
| J-70 | JR-70 | JGD-70 | J-90 |
Uvavanyo lobushushu/℃ |
| 100±2 | 100±2 | 100±2 | 135±2 |
Uvavanyo ixesha/h |
| 168 | 168 | 168 | 240 |
Amandla okuqina emva kokuguga / MPa | ≥ | 15.0 | 15.0 | 16.0 | 16.0 |
Elona qondo liphezulu lokutshintsha amandla okuqina/% |
| ±20 | ±20 | ±20 | ±20 |
Ukuxinezeleka koxinzelelo kukwaphuka emva kokuguga/% | ≥ | 150 | 180 | 150 | 150 |
Ubuninzi bezinga lokutshintsha kwe-tensile ubunzima ngexesha lekhefu/% |
| ±20 | ±20 | ±20 | ±20 |
Imeko yovavanyo |
| 100±2℃ | 100±2℃ | 100±2℃ | 115±2℃ |
|
| 168 h | 168 h | 168 h | 240 h |
Ilahleko enkulu/(g/m2) | ≤ | 20 | 20 | 20 | 20 |