Intshayelelo yemveliso: Ijeli yokuzalisa ikhebula ye-Optical ithatha i-oyile yenkqubo ye-GTL kunye nezixhobo eziphezulu ze-molecular synthetic njengezixhobo eziphambili. Zidityaniswe zibe thambileyo, i-low-viscosity, i-high thixotropic index, ijeli yokuzalisa ecacileyo engenambala ngobuchule obuphambili bemveliso eneempawu zokugxotha amanzi, ubuchwephesha obugqwesileyo bokucubungula kunye neempawu zobushushu obuphezulu kunye nobushushu obuphantsi. Iyakwazi ukugcina ithambile ngaphantsi kwe -40 ℃ kwaye akukho-driphu kubushushu obuphezulu be-80 ℃. Inkqubo yokuzalisa ilula enokuzaliswa kwiqondo lokushisa eliqhelekileyo, elifanelekileyo ngokukodwa kwi-cable sheath kunye ne-cable core. Ngokweemfuno ezahlukeneyo zabathengi, isalathisi sobugcisa be-viscosity, ukungena, i-thixotropic kunye njl.
Iiparamitha zobugcisa
I-Cold Application Optical Cable Ukuzalisa i-Gel yoBuchwephesha
1, IiMfuno zobuGcisa ngokuBanzi
Ukuzalisa i-gel iyadingeka ukuba i-homogeneous, i-hydrogen absorption, kwaye ayibandakanyi naluphi na uthuli, iincinci zetsimbi kunye nezinye izinto ezingcolileyo. Kufuneka kungabonakali amaqamza omoya, kwaye umngundo kufuneka ungabikho isondlo. Ukuzalisa i-gel kufuneka kungabi netyhefu, kungabikho ukuvuselela kwesikhumba.
2, iiparamitha zobugcisa eziphambili
intlango Inani | Izinto | iyunithi | Isalathiso |
1 | inkangeleko | I-homogeneous, akukho kungcola | |
2 | Indawo yokulahla | ℃ | ≥150 |
3 | Ubuninzi (20℃) | g/cm2 | ≤0.96 |
4 | Ukungena kweKhowuni 25℃-40℃ | 1/10mm 1/10mm | ≥300 ≥100 |
5 | Ixesha lokungeniswa kwe-oxidation (190℃) | imiz | ≥30 |
6 | Indawo edanyazayo | ℃ | >200 |
7 | Ukuvela kweHydrogen (80 ℃, 24h) | μl/g | ≤0.03 |
8 | Ukubila kwe-oyile (80 ℃, 24h) | % | ≤2.0 |
9 | Umthamo wokuphunga (80 ℃, 24h) | % | ≤1.0 |
10 | Ixesha lokufunxa 25℃(15g isampuli+10g amanzi) | imiz | ≤2.0 |
11 | Ukunciphisa 25 ℃ 5r 100g isampuli + 50g amanzi 24h | % % | ≥15 ≥70 |
12 | Ixabiso leAcid | mgK0H/g | ≤1.0 |
13 | Isiqulatho samanzi | % | ≤0.1 |
14 | i-viscosity (25℃, D=20S-1) | mpa.s | 10500-30000 |
15 | ukuhambelana: A, kunye pine casing imathiriyeli (85 ℃, 30 × 24h) B, kunye pine casing imathiriyeli (85 ℃, 45 × 24h) ukwahluka ukomelela ukomelela ngexesha lekhefu umahluko B, kunye pine casing imathiriyeli yokugquma (80 ℃), 28 × 24h) ukwahlukahlukana kokuqina kokuqina ekukhuleni kobunzima bekhefu C, Ibhendi yentsimbi ehlanganisiweyo (68 ℃, 7 × 24h) Iteyiphu ehlanganisiweyo yentsimbi, iteyiphu yeplastiki yeAluminiyam | % % % % % | akukho delamination akukho kuqhekeka ≤25 ≤30 ≤3 akukho kuqhekeka ≤25 ≤25 ≤15 akukho delamination akukho kuqhekeka |
15 | edlekayo (80 ℃, 14×24h) ngobhedu, ialuminiyam, intsimbi | Akukho ndawo zomhlwa |
3, Iimfuno zokusebenza kokusingqongileyo
Uhlobo | umcimbi | Umxholo othintelayo (mg/kg) |
Intsimbi enzima | umbhobho | ≤1000 |
ikhadmium | ≤100 | |
imekyuri | ≤1000 | |
Hexavalent chromium | ≤1000 | |
I-Organic Bromide | Iibiphenyls ezinePolybrominated (PBB) | ≤1000 |
Iipolybrominated diphenyl ethers (PBDE) | ≤1000 |