Intshayelelo yemveliso: Ijeli yokuzalisa ifayibha ye-Optical ithatha i-oyile yenkqubo ye-viscosity ephezulu ye-GTL, imathiriyeli ephezulu ye-molecular synthetic kunye ne-organic thickener njengezixhobo eziphambili. Zidityaniswe ukuba zibe yijeli yokuzalisa i-non-silicon optical fiber ngobuchule obuphambili bemveliso eneempawu zoxinzelelo oluphantsi, ukusebenza kakuhle kobushushu, i-high thixotropic index, isicelo esibanzi, ixabiso elincinci le-asidi kunye nexabiso le-hydrogen evolution. Uhlobo lwe-AC-E008 nalo lusebenza ngokuthe ngcembe lobushushu phakathi kwe -45°C ukuya kuma-80°C. Ngokweemfuno ezahlukeneyo zabathengi, isalathiso sobuchwephesha se-viscosity, ukungena, i-thixotropic kunye njl njl.
Iiparamitha zobugcisa
Isicelo esibandayo se-fiber optical filling gel inkcazo yobugcisa
1, iimfuno zobugcisa ngokubanzi
Ukuzalisa i-gel iyadingeka ukuba i-homogeneous, i-hydrogen absorption, kwaye ayibandakanyi naluphi na uthuli, iincinci zetsimbi kunye nezinye izinto ezingcolileyo. Kufuneka kungabonakali amaqamza omoya, kwaye umngundo kufuneka ungabikho isondlo. Ukuzalisa i-gel kufuneka kungabi netyhefu, kungabikho ukuvuselela kwesikhumba.
2, iiparamitha zobugcisa eziphambili
Uthotho Inani | Izinto | Iyunithi | Isalathiso |
1 | inkangeleko | I-homogeneous, akukho kungcola | |
2 | Indawo yokulahla | ℃ | ≥200 |
3 | ukuxinana(20℃) | g/i-cm2 | ≤0.88 |
4 | Ukungena kweKhowuni 25℃-40℃ | 1/10mm 1/10mm | ≥400 ≥230 |
5 | Ukuzinza kombala(130℃,120h) | ≤2.5 | |
6 | Ixesha lokungeniswa kwe-oxidation(190℃) | imiz | ≥30 |
7 | Indawo edanyazayo | ℃ | ≥220 |
8 | Ukuvela kwe-hydrogen(80℃,24h) | μl/g | ≤0.03 |
9 | Ukubila kweoli(80℃,24h) | % | ≤0.5 |
10 | Umthamo wokuphuma kwamanzi(80℃,24h) | % | ≤0.5 |
11 | Ukumelana namanzi(20℃,7d) | Ukungaqhawuki | |
12 | Ixabiso leAcid | mgK0H/g | ≤0.3 |
13 | Isiqulatho samanzi | % | ≤0.01 |
14 | i-viscosity(25℃,D=6S-1) | mpa.s | 22000±6600 |
15 | ukuhambelana:A,ngefiber optical, opticalizinto zokugquma ifiber(85℃,30×24h)B,nge pine casingizinto eziphathekayo(85℃,30×24h)Ukwahluka kubude bamandla okuqina ngexesha lokwahluka kobunzima C,Ibhendi yentsimbi ehlanganisiweyo (68℃,7×24h)Iteyiphu edibeneyo yentsimbi-yeplastiki,Iplastiki yeAluminiyamiteyiphu ehlanganisiweyo | % % % | Akukho mbala uphelayo, Akukho mfuduko, akukho delamination, akukho ukuqhekeka Ubuninzi bamandla okukhululwa 1.0N~8.9NIxabiso eliphakathi 1.0N~5.0Nakukho delamination akukho kuqhekeka ≤25 ≤30 ≤3 akukho delamination akukho kuqhekeka |
16 | edlekayo(80℃,14×24h)ngobhedu, i-aluminiyam, intsimbi | Akukho ndawo zomhlwa |
3, Iimfuno zokusebenza kokusingqongileyo
Uhlobo | umcimbi | Umxholo othintelayo(mg/kg) |
Intsimbi enzima | umbhobho | ≤1000 |
ikhadmium | ≤100 | |
imekyuri | ≤1000 | |
Hexavalent chromium | ≤1000 | |
I-Organic Bromide | Iibiphenyls zePolybrominated(UN) | ≤1000 |
Iipolybrominated diphenyl ethers(PBDE) | ≤1000 |