Polyvinyl Chloride Insulated Cable Material (PVC Insulated Cable Material)
CIRI PRODUK
RUANG PANGGUNAAN
Item tés sareng standar
abdianjeunna boga |
| J-70 | JR-70 | JGD-70 | J-90 |
kakuatan Tensile / MPa | ≥ | 15.0 | 15.0 | 16.0 | 16.0 |
Regangan tarik dina putus /% | ≥ | 150 | 180 | 150 | 150 |
Deformasi termal | ≥ | 40 | 50 | 30 | 30 |
sipat rapuh tnyaéta suhu / ℃ |
| -15 | -20 | -15 | -15 |
Dampak sipat embrittlement |
| Lulus | Lulus | Lulus | Lulus |
waktos stabilitas termal dina 200 ℃ /min | ≥ | 60 | 60 | 100 | 180 |
Résistivitas volume dina 20 ℃/Ω·m | ≥ | 1.0×10 12 | 1.0×10 11 | 3.0×1012 | 1.0×10 12 |
kakuatan diéléktrik/(MV/m) | ≥ | 20 | 20 | 25 | 20 |
Faktor leungitna diéléktrik (50Hz) | ≤ | — | — | 0.1 | — |
Uji suhu / ℃ |
| 70±1 | 70±1 | 70±1 | 95±1 |
résistansi volume/Ω·m | ≥ | 1.0×10 9 | 1.0×108 | 5.0×109 | 5.0×108 |
Sipat mékanis sareng fisik bahan kabel polivinil klorida saatos sepuh
abdianjeunna boga |
| J-70 | JR-70 | JGD-70 | J-90 |
Uji suhu / ℃ |
| 100±2 | 100±2 | 100±2 | 135±2 |
Tés waktos / jam |
| 168 | 168 | 168 | 240 |
kakuatan Tensile sanggeus sepuh / MPa | ≥ | 15.0 | 15.0 | 16.0 | 16.0 |
Laju parobahan kakuatan tensile maksimum /% |
| ±20 | ±20 | ±20 | ±20 |
Galur tegangan dina narekahan sanggeus sepuh /% | ≥ | 150 | 180 | 150 | 150 |
| Laju robah maksimum tensile galur dina putus /% |
| ±20 | ±20 | ±20 | ±20 |
Kaayaan tés |
| 100±2 ℃ | 100±2 ℃ | 100±2 ℃ | 115± 2 ℃ |
|
| 168 jam | 168 jam | 168 jam | 240 jam |
Leungitna beurat/(g/m2) | ≤ | 20 | 20 | 20 | 20 |