Haseup Rendah Nol Halogén Photovoltaic Insulasi, Sarung Bahan Kabel (LSZH Photovoltaic Insulasi, Sarung Bahan Kabel)
CIRI PRODUK
RUANG PANGGUNAAN
Item tés sareng standar
|
| Item pamariksaan | Unit | Rsyarat-syarat | ||
| WDZ-Y-J70 | WDZ-Y-H70 | WDZ-Y-H90 | |||
| 1 | Kakuatan regangan | MPa | ≥10. 0 | ≥10. 0 | ≥10. 0 |
| 2 | Elongation dina putus | % | ≥160 | ≥160 | ≥160 |
| 3 | Kamar sepuh hawa |
|
|
|
|
| Suhu sepuh | ℃ | 100±2 | 100±2 | 110±2 | |
| Waktos sepuh | h | 168 | 168 | 240 | |
| Laju maksimum parobahan kakuatan tensile | % | ±25 | ±25 | ±25 | |
| Laju maksimum parobahan elongation dina putus | % | ±25 | ±25 | ±25 | |
| 4 | Deformasi termal |
|
|
|
|
| Uji suhu | ℃ | 90±2 | 90±2 | 90±2 | |
| Hasil ékspérimén | % | ≤50 | ≤50 | ≤50 | |
| 5 | 20 ℃ résistansi volume | Duh · m | ≥1. 0×1012 | ≥1. 0×1010 | ≥1. 0×1010 |
| 6 | Résistivitas volume dina suhu operasi |
|
|
|
|
| Uji suhu | ℃ | 70±1 | — | — | |
| Résistansi volume | Duh · m | ≥2. 0×108 | — | — | |
| 7 | kakuatan diéléktrik | MV/m | ≥20 | ≥18 | ≥18 |
| 8 | Uji kejut panas |
|
|
|
|
| Uji suhu | ℃ | 130±3 | 130±3 | 130±3 | |
| waktos tés | % | 1 | 1 | 1 | |
| Hasil ékspérimén | — | Taya cracking | Taya cracking | Taya cracking | |
| 9 | Dampak suhu embrittlement |
|
|
|
|
| Uji suhu | ℃ | -25 | -25 | -25 | |
| Hasil ékspérimén | Jumlah | ≤15/30 | ≤15/30 | ≤15/30 | |
| 10 | Uji résistansi ozon |
|
|
|
|
| Uji suhu | ℃ | — | 25±2 | 25±2 | |
| waktos ékspérimén | h | — | dua puluh opat | dua puluh opat | |
| Konsentrasi ozon | ppm | — | 250~300 | 250~300 | |
| Hasil ékspérimén | — | — | Taya cracking | Taya cracking | |
| 11 | Tes immersion cai panas |
|
|
|
|
| Uji suhu | ℃ | — | 70±2 | 70±2 | |
| waktos ékspérimén | h | — | 168 | 168 | |
| Laju maksimum parobahan kakuatan tensile | % | — | ±30 | ±30 | |
| Laju maksimum parobahan elongation dina putus | % | — | ± 35 | ± 35 | |
| 12 | Indéks oksigén | % | ≥28 | ≥30 | ≥30 |
| 13 | Kapadetan haseup |
|
|
|
|
| flameless | — | ≤350 | ≤350 | ≤350 | |
| hurung | — | ≤100 | ≤100 | ≤100 | |
| 14 | Ngaduruk ngaleupaskeun kaasaman gas |
|
|
|
|
| eusi HCI jeung HBr | % | ≤0.5 | ≤0.5 | ≤0.5 | |
| eusi HF | % | ≤0.1 | ≤0.1 | ≤0.1 | |
| nilai pH | — | ≥4.3 | ≥4.3 | ≥4.3 | |
| konduktivitas listrik | μS/mm | ≤10 | ≤10 | ≤10 | |
| 15 | Bahaya karacunan haseup bahan | Numutkeun sarat aplikasi produk, disawalakeun ku pihak suplai sareng paménta. | |||