Cold Application Type Optical Cable Ho Tlatsa Gel
Kenyelletso ea Sehlahisoa
Kenyelletso ea Sehlahisoa: Gel ea ho tlatsa thapo ea Optical e nka oli ea ts'ebetso ea GTL le lisebelisoa tse phahameng tsa limolek'hule e le lisebelisoa tsa mantlha. Li kopantsoe ho ba bonolo, li-viscosity tse tlase, index e phahameng ea thixotropic, gel e se nang mebala e hlakileng ea ho tlatsa ka mokhoa o tsoetseng pele oa tlhahiso eo likarolo tsa eona li nang le ho thibela metsi, mokhoa o babatsehang oa ho sebetsa le thepa ea mocheso o phahameng le o tlaase. E ka lula e le bonolo ka tlas'a -40 ℃ 'me e se na marotholi mocheso o phahameng oa 80 ℃. Mokhoa oa ho tlatsa o bonolo o ka tlatsoang ka mocheso o akaretsang, haholo-holo o loketseng sheath ea cable le core ea cable. Ho latela litlhoko tse fapaneng tsa bareki, index ea tekheniki ea viscosity, penetration, thixotropic joalo-joalo e ka fetoloang molemong oa ho khotsofatsa litlhoko tsa mokhoa oa ho tlatsa.
Litekanyetso tsa tekheniki
Cold Application Optical Cable Ho Tlatsa Gel Tlhaloso ea Teknoloji
1, Litlhoko tse akaretsang tsa tekheniki
Ho tlatsa gel ho hlokahala hore e be homogeneous, absorption ea hydrogen, 'me ha e kenyeletse lerōle leha e le lefe, likaroloana tsa tšepe le litšila tse ling. E lokela ho se bonahale libubble tsa moea, 'me hlobo ha ea lokela ho ba phepo e nepahetseng. Ho tlatsa gel e lokela ho ba e se nang chefo, e se ke ea susumetsa letlalo.
2, lintlha tse ka sehloohong tsa tekheniki
lesupi Nomoro | Lintho | unit | Index |
1 | ponahalo | Homogeneous, ha ho na litšila | |
2 | Sebaka sa ho theoha | ℃ | ≥150 |
3 | boima ba 'mele (20℃) | g/cm2 | ≤0.96 |
4 | Khoune ho kenella 25℃-40℃ | 1 ~ 10mm 1 ~ 10mm | ≥300 ≥100 |
5 | Nako ea ho kenya oxidation (190 ℃) | min | ≥30 |
6 | Sebaka se benyang | ℃ | >200 |
7 | Hydrogen evolution (80 ℃, 24h) | μl/g | ≤0.03 |
8 | Ho fufuleloa ha oli (80 ℃, 24h) | % | ≤2.0 |
9 | Evaporation bokgoni (80 ℃, 24h) | % | ≤1.0 |
10 | Nako ea ho Absorbency 25 ℃(15g sampole+10g metsi) | min | ≤2.0 |
11 | Dilatation 25 ℃ 5r 100g sampole + 50g metsi 24h | % % | ≥15 ≥70 |
12 | Boleng ba asiti | mgK0H | ≤1.0 |
13 | Likahare tsa metsi | % | ≤0.1 |
14 | viscosity (25 ℃, D = 20S-1) | mpa.s | 10500-30000 |
15 | lumellana: A, le thepa ea phaene casing (85 ℃, 30 × 24h) B, le phaene casing lintho tse bonahalang (85 ℃, 45 × 24h) ho fapana ha tensile matla elongation ka khefu boima mefuta e fapaneng B, le phaene casing insulation thepa (80 ℃, 28 × 24h) phapano ea matla a manolotsoeng nakong ea khefu ea boima bo fapaneng C, sehlopha sa tšepe se kopantsoeng (68 ℃, 7 × 24h) Theipi e kopantsoeng ea tšepe-polasetiki, teipi ea polasetiki ea Aluminium | % % % % % | no delamination no cracking ≤25 ≤30 ≤3 no cracking ≤25 ≤25 ≤15 no delamination no cracking |
15 | e senyang (80 ℃, 14×24h) ka koporo, aluminium, tšepe | Ha ho na lintlha tsa kutu |
3, Litlhokahalo tsa ts'ebetso ea tikoloho
Mofuta | taba | Litaba tse thibelang (mg/kg) |
Tšepe e boima | liphaephe | ≤1000 |
cadmium | ≤100 | |
mercury | ≤1000 | |
Hexavalent chromium | ≤1000 | |
Bromide ea tlhaho | Polybrominated biphenyls (PBB) | ≤1000 |
Polybrominated diphenyl ethers (PBDE) | ≤1000 |