Sumo yechigadzirwa:Optical fiber yekuzadza gel inotora yakakwira viscosity GTL process mafuta, yakakwira ma molecular synthetic material uye organic thickener sechinhu chikuru. Iwo akasanganiswa kuti ave asiri-silicon optical fiber yekuzadza gel nemhando yepamusoro yekugadzira maitiro ayo akadzika density, yakanakisa tembiricha kuita, yakakwirira thixotropic index, yakafara application, diki acid kukosha uye hydrogen evolution kukosha. Type AC-E008 zvakare ine tembiricha yakadzikama iri pakati -45°C kusvika 80°C. Zvinoenderana nezvakasiyana zvinodiwa nevatengi, iyo tekinoroji index ye viscosity, kupinda, thixotropic uye nezvimwe zvinogona kugadziriswa kuitira kugutsa zvinodiwa zvekuzadza tekinoroji.
Technical parameters
Cold application optical fiber inozadza gel tekinoroji yakatarwa
1, general technical zvinodiwa
Kuzadza gel kunodiwa kuve homogeneous, hydrogen absorption, uye haisanganisi chero guruva, simbi zvimedu, uye kumwe kusvibiswa. Inofanira kunge isingaonekwi inooneka mabhubhu emhepo, uye mold haifanirwe kunge iri chikafu. Kuzadza gel kunofanira kunge kusiri-chepfu, pasina kukurudzira kune ganda.
2、mahombe tekinoroji paramita
Seri Number | Items | Unit | Index |
1 | chitarisiko | Homogeneous, hapana tsvina | |
2 | Drop point | ℃ | ≥200 |
3 | density(20 ℃) | g/cm2 | ≤0.88 |
4 | Koni kupinda 25 ℃-40 ℃ | 1/10mm 1/10mm | ≥400 ≥230 |
5 | Kugadzikana kwemavara(130 ℃,120h) | ≤2.5 | |
6 | Oxidation induction nguva(190 ℃) | min | ≥30 |
7 | Kupenya point | ℃ | ≥220 |
8 | Hydrogen evolution(80 ℃,24h) | μl/g | ≤0.03 |
9 | Kubuda kwemafuta(80 ℃,24h) | % | ≤0.5 |
10 | Evaporation capacity(80 ℃,24h) | % | ≤0.5 |
11 | Kupokana nemvura(20 ℃,7d) | Kwete-disassembly | |
12 | Asidhi kukosha | mgK0H/g | ≤0.3 |
13 | Mvura yemvura | % | ≤0.01 |
14 | viscosity(25℃,D=6S-1) | mpa.s | 22000±6600 |
15 | kugarisana:A,ine optical fiber, opticalfiber coating zvinhu(85℃,30×24h)B,ine pine casingzvinhu(85℃,30×24h)mutsauko mukurebesa kwesimba pakureba panguva yekuzorora misa kusiyanisa C,Composite simbi bhendi (68℃,7×24h)Simbi-plastiki inoumba tepi,Aluminium plastikitepi yemubatanidzwa | % % % | Hapana ruvara rwuri kupera, Hapana kutama, hapana delamination, hapana kupaza Maximum kuburitsa simba 1.0N~8.9NAvhareji kukosha 1.0N~5.0Nhapana delamination hapana kutsemuka ≤25 ≤30 ≤3 hapana delamination hapana kutsemuka |
16 | corrosive(80 ℃,14×24h)nemhangura, aluminium, simbi | Hapana corrosion points |
3, Zvinodiwa zvekushanda kwezvakatipoteredza
Type | nyaya | Prohibitive content(mg/kg) |
Heavy metal | plumbic | ≤1000 |
cadmium | ≤100 | |
mercury | ≤1000 | |
Hexavalent chromium | ≤1000 | |
Organic Bromide | Polybrominated biphenyls(UN) | ≤1000 |
Polybrominated diphenyl ethers(PBDE) | ≤1000 |