mea uaea PE

O le PE o se polyethylene faʻapipiʻi, e masani ona vaevaeina i polyethylene maualuga (HDPE), polyethylene medium density (MDPE), polyethylene low density (LDPE) ma le laina laina maualalo polyethylene (LLDPE).

Faafesootai matou

Fa'amatalaga o oloa

Faailoga o oloa

uiga oloa

1.HDPE o se ituaiga o tioata maualuga, non-polar resin thermoplastic gaosia e le ethylene copolymerization. O foliga vaaia o le HDPE muamua e lanu pa'epa'e, ma e translucent i se tulaga patino i le vaega itiiti. E sili ona tetee atu i le tele o vailaʻau faʻapitonuʻu ma fale gaosimea, ma e mafai ona tetee atu i le pala ma le faʻamavaeina o mea faʻamaʻi malosi (concentrated nitric acid), acid ma alkali masima ma solvents organic (carbon tetrachloride). O le polymer e le mitiia le susu ma e lelei le vai e tetee atu i le ausa, lea e mafai ona faʻaaogaina mo le susu ma le puipuiga o le seepage.

2.MDPE o loʻo faʻaalia i le faʻalavelave faʻaleagaina o le siosiomaga ma le faʻamalosia o le malosi umi. O le maualuga o le MDPE o le 0.926-0.953, o le tioata e 70% -80%, o le mamafa o le molecular mamafa o le 200,000, o le malosi o le tensile o le 8-24 mpa, o le elongation i le malologa o le 50% -60%, o le vevela vevela o le. 126-135 ℃, ma le fa'afefeteina o le tafe ole 0.1-35 g / 10 minute. vevela vevela (0.46 mpa)49-74℃.

3. Low density polyethylene o le ituaiga sili ona mama i polyethylene resin. Pe a faʻatusatusa i le polyethylene maualuga, o lona tioata (55% -65%) ma le faʻamaluluina (90-100 ℃) e maualalo. E i ai le vaivai lelei, fa'alautele, manino, malulu ma fa'agaoioiga. O lona mautu vailaʻau e lelei, e mafai ona tatalia acid, alkali ma masima vai vaifofo; Lelei le fa'amama eletise ma le fa'aogaina o le kasa; Fa'aitiitia le vai; Faigofie ona mu. O le meatotino e vaivai, faʻatasi ai ma le faʻalauteleina lelei, faʻapipiʻi eletise, faʻamautu vailaʻau, gaioiga faʻatinoina ma le maualalo o le vevela (tetee i -70 ℃).

4. Faʻatusatusa i le LDPE, o loʻo i ai i le LLDPE le lelei o le malosi maualuga, malosi lelei, malosi malosi, vevela vevela, malulu malulu, ma isi mea faapena. solvents organic ma isi mea faapena.

Manatua: PE palasitika vaega e faʻaaogaina lautele ma e manaʻomia ona faʻatulagaina e tusa ai ma manaʻoga o tagata faʻatau i faʻaaliga eseese.

Fa'ailoga oloa

Igoa	HDPE	LDPE	LLDPE
Sogisogi, o'ona	E le oona, leai se tofo, leai se manogi	E le oona, leai se tofo, leai se manogi	E le oona, leai se tofo, leai se manogi
Malosi	0.940~0.976g/cm³	0.910~0.940g/cm³	0.915~0.935g/cm³
Crystallinity	85%-65%	45-65%	55-65%
fausaga mole	O lo'o i ai na'o le carbon-carbon ma carbon-hydrogen bonds, lea e mana'omia ai le tele o le malosi e momotu ai	O le polymer e la'ititi le mamafa mole mole ma e mana'omia le itiiti o le malosi e momotu ai	Faiga laina, itiiti filifili lala, filifili pupuu, e manaʻomia le itiiti ifo o le malosi e momotu ai
Mea fa'amalulu	125-135 ℃	90-100 ℃	94-108 ℃
Mea tau masini	Malosi maualuga, malosi lelei, malosi malosi	Le lelei le malosi fa'ainisinia	Malosi maualuga, malosi lelei, malosi malosi
Malosi fa'asa	Maualuga	Maulalo	Maualuga
Elongation i le malologa	Maualuga	Maulalo	Maualuga
Malosi a'afiaga	Maualuga	Maulalo	Maualuga
Susū-faʻamaonia ma faʻaogaina le suavai	O loʻo i ai le faʻaogaina lelei o le vai, vai ausa ma le ea, maualalo le faʻaogaina o le vai ma le lelei o le teteʻe	Le lelei le susu ma le fa'amaluina o le ea	O loʻo i ai le faʻaogaina lelei o le vai, vai ausa ma le ea, maualalo le faʻaogaina o le vai ma le lelei o le teteʻe
Acid, alkali, corrosion, organic solvent resistance	Tete'e i le pala oxidant malosi; Tetee i le acid, alkali ma masima eseese; E le mafai ona solu i so'o se solvent organic, etc.	Acid, alkali, vaifofo masima tetee corrosion, ae le lelei solvent tetee	Tete'e i le acid, alkali ma organic solvents
Tete'e vevela/malili	Lelei le vevela ma le malulu, i le vevela o le potu ma e oʻo lava ile -40F maualalo le vevela, sili atu le malosi o le aʻafiaga, maualalo le vevela vevela vevela	Tete'e vevela maualalo, maualalo vevela embrittlement vevela	Lelei le vevela ma le malulu etetee Maulalo vevela embrittlement vevela
Tete'e i fa'alavelave fa'alesiosiomaga ta'e	Lelei	sili atu	Lelei