Uaea Fa'amalosi Autu GFRP Tagata Malosi mo Uaea Mata
Folasaga o oloa
GFRP faʻaalia tulaga lelei
GFRP fa'amatalaga autu
0.40 | 0.50 | 0.60 | 0.70 | 0.80 | 0.90 | 1.00 | 1.10 | 1.20 | 1.30 | 1.40 |
1.50 | 1.60 | 1.70 | 1.80 | 1.90 | 2.00 | 2.10 | 2.20 | 2.30 | 2.40 | 2.50 |
2.60 | 2.70 | 2.80 | 3.00 | 3.30 | 3.40 | 3.50 | 3.80 | 4.00 | 4.60 | 5.00 |
GFRP mafolafola fa'amatalaga autu
0.60x1.30mm | 0.70x3.00mm | 1.00x3.00 mm | 1.20x3.80mm | 1.27x3.00mm | 1.40x3.00mm | 1.60x3.00mm |
Fa'aputu & Teuina
Parakalafa fa'apitoa
Su'ega mea | Iunite (po'o tulaga) | Parakalafa fa'apitoa |
I fafo-o-taamilosaga | % |
|
Fa'aaliga | Leai se pupu, leai ni ta'e, lagona lamolemole | |
Fa'apalepale lautele | % | ±2 |
Kalave fa'apitoa | g/cm3 | 2.05~2.15 |
Malosi fa'asa | MPa | ≥1100 |
Tensile modulus o elasticity | GPa | ≥50 |
Malosi punou | MPa | ≥1100 |
Fa'ato'a fa'a'u'umi fa'amalosi | GPa | ≥50 |
Elongation i le malologa | % | 2.5% ≤ X ≤ 4% |
Coefficient o le faalauteleina laina | 1/℃(-30℃~+80℃) | ≤8×10-6 |
Fa'aiti'itia fua vevela | % | 0 |
Suavai | % | ≤0.1 |
La'ititi la'ititi fa'ato'a pi'o | mm(20℃±5℃) | 25D |
Meatotino punou maualuga vevela | (50D,120℃,100h) | Leai se pupu, leai ni ta'e, lagona lamolemole, leai se punou, e mafai ona puna sa'o |
Maualalo le vevela mea totino | (50D,-40℃,100h) | Leai se pupu, leai ni ta'e, lagona lamolemole, leai se punou, e mafai ona puna sa'o |
Meatotino tausaafia | ±360°/m | Le mautinoa |