Materjal tal-kejbil tal-linja tal-ġilda LSZH
KARATTERISTIĊI TAL-PRODOTT
AMBITU TA' UŻU
Oġġetti u standards tat-test
|
| Oġġett ta' spezzjoni | Unità | Rrekwiżiti | ||
| WDZ-Y-J70 | WDZ-Y-H70 | WDZ-Y-H90 | |||
| 1 | Saħħa tat-tensjoni | MPa | ≥10. 0 | ≥10. 0 | ≥10. 0 |
| 2 | Titwil fil-waqfa | % | ≥160 | ≥160 | ≥160 |
| 3 | Kamra tat-tixjiħ tal-arja |
|
|
|
|
| Temperatura tat-tixjiħ | ℃ | 100±2 | 100±2 | 110±2 | |
| Żmien tat-tixjiħ | h | 168 | 168 | 240 | |
| Rata massima ta 'bidla tas-saħħa tat-tensjoni | % | ±25 | ±25 | ±25 | |
| Rata massima ta 'bidla ta' titwil fil-waqfa | % | ±25 | ±25 | ±25 | |
| 4 | Deformazzjoni termali |
|
|
|
|
| It-temperatura tat-test | ℃ | 90±2 | 90±2 | 90±2 | |
| Riżultat sperimentali | % | ≤50 | ≤50 | ≤50 | |
| 5 | Reżistività tal-volum ta '20℃ | Oh · m | ≥1. 0×1012 | ≥1. 0×1010 | ≥1. 0×1010 |
| 6 | Reżistività tal-volum f'temperatura operattiva |
|
|
|
|
| It-temperatura tat-test | ℃ | 70±1 | — | — | |
| Reżistività tal-volum | Oh · m | ≥2. 0×108 | — | — | |
| 7 | Saħħa dielettrika | MV/m | ≥20 | ≥18 | ≥18 |
| 8 | Test ta 'xokk tas-sħana |
|
|
|
|
| It-temperatura tat-test | ℃ | 130±3 | 130±3 | 130±3 | |
| Ħin tat-test | % | 1 | 1 | 1 | |
| Riżultat sperimentali | — | Ebda qsim | Ebda qsim | Ebda qsim | |
| 9 | Temperatura ta 'fraġilità ta' l-impatt |
|
|
|
|
| It-temperatura tat-test | ℃ | -25 | -25 | -25 | |
| Riżultat sperimentali | Numru | ≤15/30 | ≤15/30 | ≤15/30 | |
| 10 | Test tar-reżistenza għall-ożonu |
|
|
|
|
| It-temperatura tat-test | ℃ | — | 25±2 | 25±2 | |
| Ħin tal-esperiment | h | — | Erbgha u ghoxrin | Erbgha u ghoxrin | |
| Konċentrazzjoni tal-ożonu | ppm | — | 250 ~ 300 | 250 ~ 300 | |
| Riżultat sperimentali | — | — | Ebda qsim | Ebda qsim | |
| 11 | Test ta 'immersjoni ta' ilma sħun |
|
|
|
|
| It-temperatura tat-test | ℃ | — | 70±2 | 70±2 | |
| Ħin tal-esperiment | h | — | 168 | 168 | |
| Rata massima ta 'bidla tas-saħħa tat-tensjoni | % | — | ±30 | ±30 | |
| Rata massima ta 'bidla ta' titwil fil-waqfa | % | — | ±35 | ±35 | |
| 12 | Indiċi tal-ossiġnu | % | ≥28 | ≥30 | ≥30 |
| 13 | Densità tad-duħħan |
|
|
|
|
| bla fjamma | — | ≤350 | ≤350 | ≤350 | |
| fjamma | — | ≤100 | ≤100 | ≤100 | |
| 14 | Il-kombustjoni tirrilaxxa l-aċidità tal-gass |
|
|
|
|
| Kontenut ta' HCI u HBr | % | ≤0.5 | ≤0.5 | ≤0.5 | |
| Kontenut HF | % | ≤0.1 | ≤0.1 | ≤0.1 | |
| valur pH | — | ≥4.3 | ≥4.3 | ≥4.3 | |
| Konduttività elettrika | μS/mm | ≤10 | ≤10 | ≤10 | |
| 15 | Perikli ta' tossiċità materjali tad-duħħan | Skont ir-rekwiżiti tal-applikazzjoni tal-prodott, innegozjat mill-partijiet tal-provvista u d-domanda. | |||