Polyvinyl Chloride Insulated Cable Material (PVC Insulated Cable Material)
PRODUCT FEATURES
SPATIUM USUS
Test items et signa
egohabet |
| J-70 | JR-70 | JGD-70 | J-90 |
Distrahentes vires / MPa * | ≥ | 15.0 | 15.0 | 16.0 | 16.0 |
Distensum iactabantur confractus /% | ≥ | 150 | 180 | 150 | 150 |
Deformatio scelerisque | ≥ | 40 | 50 | 30 | 30 |
Res fragilis ttemperatus est / |
| -15 | -20 | -15 | -15 |
Impact embrittere possessiones |
| Transi | Transi | Transi | Transi |
Stabilitas scelerisque tempus at 200℃/min | ≥ | 60 | 60 | 100 | 180 |
Volumen resistentiae apud 20℃/Ω·m | ≥ | 1.010 12 | 1.010 11 | 3.01012 | 1.010 12 |
Dieelectric vi/(MV/m) | ≥ | 20 | 20 | 25 | 20 |
Dielectric damnum factor(50Hz) | ≤ | - | - | 0.1 | - |
Test temperatus/ |
| 70±1 | 70±1 | 70±1 | 95±1 |
Volumen resistivity/Ω·m | ≥ | 1.010 9 | 1.0108 | 5.0109 | 5.0108 |
Mechanica et physica polyvinyli materiae chloridi funeri post senescit
egohabet |
| J-70 | JR-70 | JGD-70 | J-90 |
Test temperatus/ |
| 100±2 | 100±2 | 100±2 | 135±2 |
Test tempus / h * |
| 168 | 168 | 168 | 240 |
Post senescit vires distrahentes / MPa | ≥ | 15.0 | 15.0 | 16.0 | 16.0 |
Maxime distrahentes vires mutationem rate /% |
| ±20 | ±20 | ±20 | ±20 |
Distrahentes ad fracturam cum senescit /% | ≥ | 150 | 180 | 150 | 150 |
Maxime mutatio rate distrahentes intendere confractus /% |
| ±20 | ±20 | ±20 | ±20 |
Test conditio |
| 100±2℃ | 100±2℃ | 100±2℃ | 115±2℃ |
|
| 168 h | 168 h | 168 h | 240 h |
Massa damna/(g/m2) | ≤ | 20 | 20 | 20 | 20 |