Ngwa oyi Optical Fiber Filling Gel
Okwu Mmalite ngwaahịa
Okwu mmeghe: Optical fiber na-ejuputa gel na-anakwere mmanụ usoro viscosity GTL dị elu, ihe sịntetik dị elu na thickener organic dị ka isi ihe. A na-ejikọta ha ka ọ bụrụ gel na-enweghị silicon optic fiber na-ejuputa gel site na usoro mmepụta dị elu nke njirimara ya dị ntakịrị, arụmọrụ okpomọkụ dị mma, nnukwu thixotropic index, ngwa obosara, uru obere acid na uru evolushọn hydrogen. Ụdị AC-E008 na-arụkwa ọrụ okpomọkụ nke ọma n'etiti -45°C ruo 80°C. Dị ka ihe dị iche iche chọrọ nke ndị ahịa, teknuzu index nke viscosity, penetration, thixotropic na wdg nwere ike gbanwee iji mejuo chọrọ nke ndochi usoro.
Usoro nka
Ngwa oyi ngwa anya fiber na-ejuputa gel nkọwa nka
1, General teknuzu chọrọ
Idochi gel dị mkpa ka ọ bụrụ otu, nnabata hydrogen, na anaghị agụnye uzuzu ọ bụla, irighiri ígwè, na adịghị ọcha ndị ọzọ. Ọ ga-abụ ọ dịghị anya anya ikuku egosipụta, na ebu kwesịrị ịbụ ihe oriri. Na-ejuputa gel kwesịrị ịbụ ihe na-adịghị egbu egbu, ọ dịghị mkpali na akpụkpọ ahụ.
2, isi oru parameters
Oghere Usoro Nọmba | Ihe | Nkeji | Index |
1 | ọdịdị | Homogeneous, enweghị adịghị ọcha | |
2 | Ebe nkwụsị | ℃ | ≥200 |
3 | njupụta(20 ℃) | g/cm2 | ≤0.88 |
4 | Ntinye cone 25 ℃-40 ℃ | 1/10mm 1/10mm | ≥400 ≥230 |
5 | Nkwụsi ike agba(130 ℃,120h) | ≤2.5 | |
6 | Oge ntinye oxidation(190 ℃) | min | ≥30 |
7 | Ebe na-egbuke egbuke | ℃ | ≥220 |
8 | Hydrogen evolushọn(80 ℃,24h) | μl/g | ≤0.03 |
9 | Mmanụ na-erugharị(80 ℃,24h) | % | ≤0.5 |
10 | Ike evaporation(80 ℃,24h) | % | ≤0.5 |
11 | Mmiri na-eguzogide(20 ℃,7d) | Enweghị ikewapụ | |
12 | Uru acid | mgK0H/g | ≤0.3 |
13 | Ọdịnaya mmiri | % | ≤0.01 |
14 | viscosity(25 ℃,D=6S-1) | mpa.s | 22000±6600 |
15 | ndakọrịta:A,na ngwa anya eriri, ngwa anyaihe mkpuchi eriri(85 ℃,30×24h)B,na pine casingihe(85 ℃,30×24h)mgbanwe na ike tensile elongation na nkwụsịtụ uka mgbanwe C,Ngwakọta igwe ejikọtara ọnụ (68 ℃,7 × 24h)Teepu mejupụtara ígwè-plastic,Aluminom plastikteepu ngwakọta | % % % | Enweghị agba na-ada ada, Enweghị mbugharị, enweghị delamination, enweghị mgbawa ike mwepụta kacha 1.0N~8.9NNkezi uru 1.0N~5.0Nno delamination no cracking ≤25 ≤30 ≤3 no delamination no cracking |
16 | na-emebi emebi(80 ℃,14 × 24h)na ọla kọpa, aluminum, ígwè | Enweghị ntụpọ corrosion |
3, Environmental arụmọrụ chọrọ
Ụdị | okwu | Ọdịnaya mmachibidoro(mg/kg) |
Igwe dị arọ | plumbic | ≤1000 |
cadmium | ≤100 | |
mercury | ≤1000 | |
chromium hexavalent | ≤1000 | |
Organic Bromide | Polybrominated biphenyls(UN) | ≤1000 |
Polybrominated diphenyl ethers(PBDE) | ≤1000 |