Cold Application Type Optical Cable Filling Gel
Gabatarwar Samfur
Gabatarwar samfur: Gel mai cike da kebul na gani yana ɗaukar mai sarrafa GTL da babban kayan roba na kwayoyin halitta azaman babban kayan tushe. An haɗu da su don zama mai laushi, ƙananan danko, babban ma'aunin thixotropic, gel mai cike da launi mara launi ta hanyar fasahar samarwa ta ci gaba wanda fasalinsa yana da ƙarancin ruwa, ingantacciyar fasahar sarrafa kayan aiki da haɓaka-da-ƙananan zafin jiki. Yana iya kiyaye taushi a ƙarƙashin -40 ℃ kuma babu-drip akan babban zafin jiki na 80 ℃. Tsarin cikawa yana da sauƙi wanda za'a iya cika shi a zafin jiki na gabaɗaya, musamman dacewa da kebul na kebul na kebul na kebul na musamman. Dangane da buƙatun daban-daban na abokan ciniki, ƙididdigar fasaha na danko, shiga, thixotropic da sauransu waɗanda za a iya daidaita su don biyan buƙatun fasaha na cikawa.
Siffofin fasaha
Cold Application Optical Cable Cika Gel Ƙayyadaddun Fasaha
1.General Technical Bukatun
Ana buƙatar gel ɗin cikawa don zama mai kama da juna, ɗaukar hydrogen, kuma baya haɗa da ƙura, barbashi na ƙarfe, da sauran ƙazanta. Ya kamata ba gani a bayyane iska kumfa, kuma mold kamata ba abinci mai gina jiki. Gel ɗin cika ya kamata ya zama mara guba, babu abin ƙarfafawa ga fata.
2, main fasaha sigogi
qasar banza Lamba | Abubuwa | naúrar | Fihirisa |
1 | bayyanar | Homogeneous, babu ƙazanta | |
2 | Wurin saukewa | ℃ | ≥150 |
3 | yawa (20 ℃) | g:cm ku2 | ≤0.96 |
4 | Shigar mazugi 25 ℃ ℃ 40 ℃ | 1: 10mm 1: 10mm | ≥300 ≥100 |
5 | Lokacin shigar Oxidation (190 ℃) | min | ≥30 |
6 | Wurin walƙiya | ℃ | >200 |
7 | Juyin Halittar Hydrogen (80℃, 24h) | μl g | ≤0.03 |
8 | Oil perspiring (80 ℃, 24h) | % | ≤2.0 |
9 | Ƙarfin ƙura (80 ℃, 24h) | % | ≤1.0 |
10 | Lokacin sha 25 ℃ (15g samfurin + 10g ruwa) | min | ≤2.0 |
11 | Dilatation 25 ℃ 5r 100g samfurin + 50g ruwa 24h | % % | ≥15 ≥70 |
12 | darajar acid | mgK0H g | ≤1.0 |
13 | Abun ciki na ruwa | % | ≤0.1 |
14 | danko (25 ℃, D=20S-1) | mpa.s | 10500-30000 |
15 | karfinsu: A, tare da Pine casing abu (85 ℃, 30 × 24h) B, tare da Pine casing abu (85 ℃, 45 × 24h) bambancin a tensile ƙarfi elongation a hutu taro bambancin B, tare da Pine casing abu $ 80 28 × 24h) bambancin a tensile ƙarfi elongation a hutu taro bambancin C, Hadakar karfe band (68 ℃, 7 × 24h) Karfe-roba hada tef, Aluminum filastik fili tef | % % % % % | no delamination no cracking ≤25 ≤30 ≤3 babu fasa ≤25 ≤25 ≤15 |
15 | m (80 ℃, 14 × 24h) da jan karfe, aluminum, karfe | Babu maki lalata |
3. Muhalli yi bukatun
Nau'in | al'amari | Abubuwan da aka haramta (mg/kg) |
Karfe mai nauyi | plumbic | ≤1000 |
cadmium | ≤100 | |
mercury | ≤1000 | |
Hexavalent chromium | ≤1000 | |
Organic Bromide | Polybrominated biphenyls (PBB) | ≤1000 |
Polybrominated diphenyl ethers (PBDE) | ≤1000 |