Cold Application Type Optical Cable Filling Gel
Product Introduction
Product introduction:Optical cable filling gel adopts GTL process oil and high molecular synthetic material as main base materials. They are combined to be soft, low-viscosity, high thixotropic index, colorless transparent filling gel by advanced production technique whose features has water repellency, excellent processing technic and high- and-low temperature properties. It can keep soft under -40℃ and no-drip on the high temperature of 80℃. Filling process is simple which can be filled at general temperature, especially suitable for particular cable sheath and cable core. According to various requirements of clients, the technical index of viscosity, penetration, thixotropic and etc. that could be adjust in order to satisfy requirements of filling technique.
Technical parameters
Cold Application Optical Cable Filling Gel Technical Specification
1、General Technical Requirements
Filling gel is needed to be homogeneous, hydrogen absorption, and does not include any dust, metal particles, and other impurities. It should be no sight visible air bubbles, and the mold should be no nutrition. Filling gel should be non-toxic, no stimulation to the skin.
2、main technical parameters
erial Number |
Items |
unit |
Index |
1 |
appearance | Homogeneous, no impurities | |
2 |
Dropping point |
℃ |
≥150 |
3 |
density(20℃) |
g/cm2 |
≤0.96 |
4 |
Cone penetration 25℃ -40℃ |
1/10mm 1/10mm |
≥300 ≥100 |
5 |
Oxidation induction time (190℃) |
min |
≥30 |
6 |
Flashing point |
℃ |
>200 |
7 |
Hydrogen evolution (80℃、24h) |
μl/g |
≤0.03 |
8 |
Oil perspiring(80℃、24h) |
% |
≤2.0 |
9 |
Evaporation capacity (80℃、24h) |
% |
≤1.0 |
10 |
Absorbency Time 25℃(15g sample+10g water) |
min |
≤2.0 |
11 |
Dilatation 25℃ 5r 100g sample+50g water 24h |
% % |
≥15 ≥70 |
12 |
Acid value |
mgK0H/g |
≤1.0 |
13 |
Water content |
% |
≤0.1 |
14 |
viscosity(25℃、D=20S-1) |
mpa.s |
10500-30000 |
15 |
compatibility: A、 with pine casing material (85℃、30×24h) B、with pine casing material (85℃、45×24h) variation in tensile strength elongation at break mass variation B、 with pine casing insulation material(80℃、28×24h) variation in tensile strength elongation at break mass variation C、 Composite metal band (68℃、7×24h) Steel-plastic composite tape、Aluminum plastic compound tape |
% % % % % |
no delamination no cracking ≤25 ≤30 ≤3 no cracking ≤25 ≤25 ≤15 no delamination no cracking |
15 |
corrosive(80℃、14×24h) with copper, aluminum, steel | No corrosion points |
3、Environmental performance requirements
Type |
matter |
Prohibitive content(mg/kg) |
Heavy metal |
plumbic | ≤1000 |
cadmium | ≤100 | |
mercury | ≤1000 | |
Hexavalent chromium | ≤1000 | |
Organic Bromide |
Polybrominated biphenyls(PBB) | ≤1000 |
Polybrominated diphenyl ethers(PBDE) | ≤1000 |